Key Points of Rubber Mastication and Mixing Technology

The processes of rubber mastication and mixing are the core stages in rubber processing, directly influencing the final Toradh quality.

1. Mastication

Raw rubber must undergo mastication to achieve suitable plasticity. For molded Táirgeacht, the desired plasticity is approximaBéim ary 0.25–0.35, while calendering and extrusion processes require around 0.4–0.6. Insufficient plasticity causes processing difficulties, whereas excessive mastication can reduce Toradh performance.
GenerUiley, rubber with a Mooney viscosity above 80—such as natural rubber (NR) or hard nitrile rubber (NBR)—requires mastication. The process should be conducted at low temperatures (below 50 °C for NR, around 40 °C for NBR) with proper roll gap and time control to Ruaent overheating. After mastication, the Cumaisc rubair should have a smooth surface and be rested for 8 hours before use.

2. Mixing

The quality of mixing determines the performance of the final rubber Toradh. The key is to ensure uniform dispersion of compounding agents, strict adherence to the ingredient addition sequence, accurate weighing, and proper control of the compound batch volume.
Common issues such as poor dispersion, blooming, scorching, and hardness variation are often caused by improper operation or inadequate process control.

3. Open Mill Operation Essentials

After the raw rubber is wrapped around the rolls for mastication, the following additives are incorporated sequentiUiley: antioxidants, accelerators, zinc oxide, carbon black, and softeners (added alternaBéim ary). FinUiley, add the curing agent (vulcanizing agent).
After mixing, perform sheeting and thin passing (with a roll gap of 0.1–0.5 mm) to ensure uniform dispersion, then cool and sheet off the compound.

4. Conclusion

High-quality rubber Táirgeacht depend on both scientific compound formulation and standardized process operation. Only through the close integration of technology and craftsmanship can the rubber manufacturing industry achieve high-quality development.

The processes of rubber mastication and mixing are the core stages in rubber processing, directly influencing the final Toradh quality.